- R841 Neodymium Magnets, 1/2 inch od x 1/4 inch id x 1/16 inch thick
- B888PC-PUR Plastic Coated Neodymium Magnets
- B75x20x5mm Neodymium Magnet, 75 x 20 x 5mm Block Magnet
- D40x30mm Neodymium Magnet, 40 x 30mm Disc Magnet
- DX2E Neodymium Magnets, 1 1/8 inch dia. x 7/8 inch thick
- DX08DIA Neodymium Magnets, 1 inch dia. x 1/2 inch thick
- B100x10x5mm Neodymium Magnet, 100 x 10 x 5mm Block Magnet
- D41AD-P Neodymium Magnets, 1/4 inch dia. x 1/16 inch thick with adhesive backing
- C-D50.8H50.8-N50 Neodymium Magnet, 50.8x50.8mm Cylinder Magnet
- C-D6H12-N45 Neodymium Magnet, 6x12mm Cylinder Magnet
D201-N52 Neodymium Magnets, 1/8 inch dia. x 1/32 inch thick
Item No.: | ALB-D201-N52 |
---|---|
Material: | NdFeB, Grade N52 |
Shape: | Disc |
Dimension: | 1/8" dia. x 1/32" thick (3.18mm dia. X 0.79mm thick) |
Tolerances: | ±0.004" x ±0.004" (±0.1mm x ±0.1mm) |
Weight: | 0.05 g |
Grade: | N52 |
Coating: | Ni-Cu-Ni (Nickel) |
Pull Force(lbs): | 0.25 lbs |
Surface Field(Gauss): | 3309 Gauss |
Magnetization direction: | Axial (Poles on Flat Ends) |
Max Operating Temp: | 80°C |
Product Drawing: | ![]() ![]() |
Previous: D201 Neodymium Magnets, 1/8 inch dia. x 1/32 inch thick
Next: D203 Neodymium Magnets, 1/8 inch dia. x 3/32 inch thick
Related Magnets
Other Grade D201 Neodymium Magnets (1/8" dia. x 1/32" thick):
Grade | Item No. | Product Name | Pull Force | Inquiry |
---|---|---|---|---|
N35 | ALB-D201-N35 | D201-N35 Neodymium Magnets | 0.29 lbs | Inquiry |
N38 | ALB-D201-N38 | D201-N38 Neodymium Magnets | 0.29 lbs | Inquiry |
N40 | ALB-D201-N40 | D201-N40 Neodymium Magnets | 0.32 lbs | Inquiry |
N42 | ALB-D201 | D201 Neodymium Magnets | 0.35 lbs | Inquiry |
N45 | ALB-D201-N45 | D201-N45 Neodymium Magnets | 0.38 lbs | Inquiry |
N48 | ALB-D201-N48 | D201-N48 Neodymium Magnets | 0.40 lbs | Inquiry |
N50 | ALB-D201-N50 | D201-N50 Neodymium Magnets | 0.42 lbs | Inquiry |
N52 | ALB-D201-N52 | D201-N52 Neodymium Magnets | 0.44 lbs | Inquiry |
N42SH | ALB-D201SH | D201SH Neodymium Magnets | 0.35 lbs | Inquiry |
High Temperature D201 Neodymium Magnets (1/8" dia. x 1/32" thick) are also available:
Neodymium Material Type | Maximum Operating Temp | Curie Temp |
---|---|---|
N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
D201 Neodymium Magnets (1/8" dia. x 1/32" thick) with other Coating are also available:
Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
---|---|---|---|
Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.