2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
United States
E-mail: sales@albmagnets.com
- SBX0X06-IN Neodymium Magnets, 1 inch length x 1 inch width x 3/8 inch thick, with step IN
- B40x20x1mm Neodymium Magnet, 40 x 20 x 1mm Block Magnet
- D74 Neodymium Magnets, 7/16 inch dia. x 1/4 inch thick
- B30x3x2mm Neodymium Magnet, 30 x 3 x 2mm Block Magnet
- S7 Neodymium Magnets, 7/16 inch diameter
- D4X0-ND Neodymium Magnets, 1/4 inch dia. x 1 inch thick
- B-W2.8H2.5L10-N50 Neodymium Magnet, 10x2.8x2.5mm Block Magnet
- DX84-N52 Neodymium Magnets, 1 1/2 inch dia. x 1/4 inch thick
- B10x3x1mm Neodymium Magnet, 10 x 3 x 1mm Block Magnet
- RC22CS-N Neodymium Magnets, 3/4 inch od x 1/8 inch id x 1/8 inch thick with countersunk hole for #8 screw
- Magnets Safety Warnings
- 5mm Magnetic Balls
- 4mm Cube Magnets
- 5x1 N48 Magnets
- 4 Differences Between Neodymium Magnets And Samarium Cobalt Magnets
- Ball And Sphere Magnets
- 1 Inch Cube Neodymium Magnets
- Scientists Create Ultra-Powerful Magnetic Field
- Where Can I Buy Large Magnets?
- Magnetization Direction For Neodymium Magnets
BZX0Y08 Neodymium Magnets, 4 inch x 2 inch x 1/2 inch thick
| Item No.: | ALB-BZX0Y08 |
|---|---|
| Material: | NdFeB, Grade N42 |
| Shape: | Block |
| Dimension: | 4" x 2" x 1/2" thick (101.6mm x 50.8mm x 12.7mm thick) |
| Tolerances: | ±0.004" x ±0.004" x ±0.004" (±0.1mm x ±0.1mm x ±0.1mm) |
| Weight: | 17.34 oz. (491.7 g) |
| Grade: | N42 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 158.70 lbs |
| Surface Field(Gauss): | 2185 Gauss |
| Magnetization direction: | Through Thickness |
| Max Operating Temp: | 80°C |
| Product Drawing: |  ·  |
Previous: BZX0Y04 Neodymium Magnets, 4 inch x 2 inch x 1/4 inch thick
Next: BZX0Y08-N52 Neodymium Magnets, 4 inch x 2 inch x 1/2 inch thick
Related Magnets
BZX0Y0X0-N52 Neodymium Magnets, 4 inch x 2 inch x 1 inch thick
BZX0Y0Y0-N52 Neodymium Magnets, 4 inch x 2 inch x 2 inch thick
BZX0Z08-N52 Neodymium Magnets, 4 inch x 3 inch x 1/2 inch thick
BZX0Z0X0-N52 Neodymium Magnets, 4 inch x 3 inch x 1 inch thickOther Grade BZX0Y08 Neodymium Magnets (4" x 2" x 1/2" thick):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-BZX0Y08-N35 | BZX0Y08-N35 Neodymium Magnets | 120.09 lbs | Inquiry |
| N38 | ALB-BZX0Y08-N38 | BZX0Y08-N38 Neodymium Magnets | 120.09 lbs | Inquiry |
| N40 | ALB-BZX0Y08-N40 | BZX0Y08-N40 Neodymium Magnets | 130.22 lbs | Inquiry |
| N42 | ALB-BZX0Y08 | BZX0Y08 Neodymium Magnets | 142.92 lbs | Inquiry |
| N45 | ALB-BZX0Y08-N45 | BZX0Y08-N45 Neodymium Magnets | 153.95 lbs | Inquiry |
| N48 | ALB-BZX0Y08-N48 | BZX0Y08-N48 Neodymium Magnets | 165.39 lbs | Inquiry |
| N50 | ALB-BZX0Y08-N50 | BZX0Y08-N50 Neodymium Magnets | 172.46 lbs | Inquiry |
| N52 | ALB-BZX0Y08-N52 | BZX0Y08-N52 Neodymium Magnets | 179.67 lbs | Inquiry |
| N42SH | ALB-BZX0Y08SH | BZX0Y08SH Neodymium Magnets | 142.92 lbs | Inquiry |
High Temperature BZX0Y08 Neodymium Magnets (4" x 2" x 1/2" thick) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
BZX0Y08 Neodymium Magnets (4" x 2" x 1/2" thick) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
Website: www.albmagnets.com
E-mail: sales@albmagnets.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.