- R822CS-P Neodymium Magnets, 1/2" od x 1/8" thick with countersunk hole for #4 screw
- D59 Neodymium Magnets, 5/16" dia. x 9/16" thick
- BY041 Neodymium Magnets, 2" x 1/4" x 1/16" thick
- BY0Y0X8 Neodymium Magnets, 2" x 2" x 1 1/2" thick
- Magnetic Motor Parts - DK Series Outer Rotor
- D96 Neodymium Magnets, 9/16" dia. x 3/8" thick
- S7 Neodymium Magnets, 7/16" diameter
- MMS-A-XC Standard Mounting Magnets
- DXCE Neodymium Magnets, 1 3/4" dia. x 7/8" thick
- SBCC6-IN Neodymium Magnets, 3/4" length x 3/4" width x 3/8" thick, with step IN
- Neodymium Disc Magnets Table
- Which fishing magnets should you buy
- Neodymium Magnets Applications
- What are neodymium magnets?
- How to choose permanent magnet?
- Neodymium Magnets (NdFeB)
- 4 Differences Between Neodymium Magnets And Samarium Cobalt Magnets
- What are Ferrite Magnets?
- Neodymium Magnets Grades
- Neodymium Block & Bar Magnets Table
B332 Neodymium Magnets, 3/16" x 3/16" x 1/8" thick
| Item No.: | ALB-B332 |
|---|---|
| Material: | NdFeB, Grade N42 |
| Shape: | Block |
| Dimension: | 3/16" x 3/16" x 1/8" thick |
| Tolerances: | ±0.004"x ±0.004"x ±0.004" |
| Weight: | 0.5401 g |
| Grade: | N42 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 2.37 lbs |
| Surface Field(Gauss): | 5052.65 Gauss |
| Magnetization direction: | Through Thickness |
| Max Operating Temp: | 80°C |
Previous: B324 Neodymium Magnets, 3/16" x 1/8" x 1/4" thick
Next: B334 Neodymium Magnets, 3/16" x 3/16" x 1/4" thick
Related Magnets
BY0Y0A Neodymium Magnets, 2" x 2" x 5/8" thick
BX044 Neodymium Magnets, 1" x 1/4" x 1/4" thick
B22C Neodymium Magnets, 1/8" x 1/8" x 3/4" thick
BY044 Neodymium Magnets, 2" x 1/4" x 1/4" thickOther Grade B332 Neodymium Magnets (3/16" x 3/16" x 1/8" thick):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-B332-N35 | B332-N35 Neodymium Magnets | 1.99 lbs | Inquiry |
| N38 | ALB-B332-N38 | B332-N38 Neodymium Magnets | 1.99 lbs | Inquiry |
| N40 | ALB-B332-N40 | B332-N40 Neodymium Magnets | 2.16 lbs | Inquiry |
| N42 | ALB-B332 | B332 Neodymium Magnets | 2.37 lbs | Inquiry |
| N45 | ALB-B332-N45 | B332-N45 Neodymium Magnets | 2.55 lbs | Inquiry |
| N48 | ALB-B332-N48 | B332-N48 Neodymium Magnets | 2.74 lbs | Inquiry |
| N50 | ALB-B332-N50 | B332-N50 Neodymium Magnets | 2.86 lbs | Inquiry |
| N52 | ALB-B332-N52 | B332-N52 Neodymium Magnets | 2.98 lbs | Inquiry |
| N42SH | ALB-B332SH | B332SH Neodymium Magnets | 2.37 lbs | Inquiry |
High Temperature B332 Neodymium Magnets (3/16" x 3/16" x 1/8" thick) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
B332 Neodymium Magnets (3/16" x 3/16" x 1/8" thick) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
Website: www.albmagnets.com
E-mail: sales@albmagnets.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.