2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
United States
E-mail: sales@albmagnets.com
- B20x5x3mm Neodymium Magnet, 20 x 5 x 3mm Block Magnet
- RX08X0 Neodymium Magnets, 1 inch od x 1/2 inch id x 1 inch thick
- R848 Neodymium Magnets, 1/2 inch od x 1/4 inch id x 1/2 inch thick
- MM-B-60 Metric Mounting Magnets
- DZ03 Neodymium Magnets, 3 inch dia. x 3/16 inch thick
- RX038DCB-N52 Neodymium Magnets, 1 inch od x 0.195 inch id x 0.375 inch id x 1/2 inch thick
- BY0X04-N52 Neodymium Magnets, 2 inch x 1 inch x 1/4 inch thick
- D6x1.5mm Neodymium Magnet, 6 x 1.5mm Disc Magnet
- D2X0 Neodymium Magnets, 1/8 inch dia. x 1 inch thick
- D47 Neodymium Magnets, 1/4 inch dia. x 7/16 inch thick
D-D19.05H6.35-N52 Neodymium Magnet, 19.05x6.35mm Disc Magnet
| Item No.: | ALB-D-D19.05H6.35-N52 |
|---|---|
| Material: | NdFeB, Grade N52 |
| Shape: | Disc |
| Dimension: | 19.05mm dia. x 6.35mm thick |
| Tolerances: | ±0.1mm x ±0.1mm |
| Weight: | 13.574g |
| Grade: | N52 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 19.98 lbs (9.08kg) |
| Surface Field(Gauss): | 3994 Gauss |
| Magnetization direction: | Axial (Poles on Flat Ends) |
| Max Operating Temp: | 80ºC |
| Product Drawing: |  ·  |
Previous: D-D18H15-N48 Neodymium Magnet, 18x15mm Disc Magnet
Next: D-D20H1-N35 Neodymium Magnet, 20x1mm Disc Magnet
Related Magnets
D-D20H1-N50 Neodymium Magnet, 20x1mm Disc Magnet
D-D20H2-N42 Neodymium Magnet, 20x2mm Disc Magnet
D-D20H3-N42 Neodymium Magnet, 20x3mm Disc MagnetOther Grade D-D19.05H6.35 Neodymium Magnets (19.05mm dia. x 6.35mm thick):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-D-D19.05H6.35-N35 | D-D19.05H6.35-N35 Neodymium Magnets | 14.11 lbs (6.41kg) | Inquiry |
| N38 | ALB-D-D19.05H6.35-N38 | D-D19.05H6.35-N38 Neodymium Magnets | 14.11 lbs (6.41kg) | Inquiry |
| N40 | ALB-D-D19.05H6.35-N40 | D-D19.05H6.35-N40 Neodymium Magnets | 15.30 lbs (6.95kg) | Inquiry |
| N42 | ALB-D-D19.05H6.35 | D-D19.05H6.35 Neodymium Magnets | 16.79 lbs (7.63kg) | Inquiry |
| N45 | ALB-D-D19.05H6.35-N45 | D-D19.05H6.35-N45 Neodymium Magnets | 17.82 lbs (8.10kg) | Inquiry |
| N48 | ALB-D-D19.05H6.35-N48 | D-D19.05H6.35-N48 Neodymium Magnets | 18.89 lbs (8.58kg) | Inquiry |
| N50 | ALB-D-D19.05H6.35-N50 | D-D19.05H6.35-N50 Neodymium Magnets | 19.43 lbs (8.83kg) | Inquiry |
| N52 | ALB-D-D19.05H6.35-N52 | D-D19.05H6.35-N52 Neodymium Magnets | 19.98 lbs (9.08kg) | Inquiry |
| N42SH | ALB-D-D19.05H6.35SH | D-D19.05H6.35SH Neodymium Magnets | 16.79 lbs (7.63kg) | Inquiry |
High Temperature D-D19.05H6.35 Neodymium Magnets (19.05mm dia. x 6.35mm thick) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
D-D19.05H6.35 Neodymium Magnets (19.05mm dia. x 6.35mm thick) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
Website: www.albmagnets.com
E-mail: sales@albmagnets.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.