2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
United States
E-mail: sales@albmaterials.com
- B5x3x1.7mm Neodymium Magnet, 5 x 3 x 1.7mm Block Magnet
- DBA Neodymium Magnets, 11/16 inch dia. x 5/8 inch thick
- DD9 Neodymium Magnets, 13/16 inch dia. x 9/16 inch thick
- BCCC-N52 Neodymium Magnets, 3/4 inch x 3/4 inch x 3/4 inch thick
- B888-3 Neodymium Magnets, 1/2 inch x 1/2 inchx 1/2 inch (- 3/16 inch hole)
- MM-B-16 Metric Mounting Magnets
- MM-D-16 Metric Mounting Magnets
- B40x30x5mm Neodymium Magnet, 40 x 30 x 5mm Block Magnet
- B15x10x2mm Neodymium Magnet, 15 x 10 x 2mm Block Magnet
- B443 Neodymium Magnets, 1/4 inch x 1/4 inch x 3/16 inch thick
D-D12.7H0.79-N52 Neodymium Magnet, 12.7x0.79mm Disc Magnet
| Item No.: | ALB-D-D12.7H0.79-N52 |
|---|---|
| Material: | NdFeB, Grade N52 |
| Shape: | Disc |
| Dimension: | 12.7mm dia. x 0.79mm thick |
| Tolerances: | ±0.1mm x ±0.1mm |
| Weight: | 0.751g |
| Grade: | N52 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 1.66 lbs (0.75kg) |
| Surface Field(Gauss): | 889 Gauss |
| Magnetization direction: | Axial (Poles on Flat Ends) |
| Max Operating Temp: | 80ºC |
| Product Drawing: |  ·  |
Previous: D-D12H10-N42 Neodymium Magnet, 12x10mm Disc Magnet
Next: D-D12.7H3.175-N50 Neodymium Magnet, 12.7x3.175mm Disc Magnet
Related Magnets
D-D12.7H3.175-N52 Neodymium Magnet, 12.7x3.175mm Disc Magnet
D-D12.7H6.35/BK Neodymium Magnet, 12.7x6.35mm Disc MagnetOther Grade D-D12.7H0.79 Neodymium Magnets (12.7mm dia. x 0.79mm thick):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-D-D12.7H0.79-N35 | D-D12.7H0.79-N35 Neodymium Magnets | 1.17 lbs (0.53kg) | Inquiry |
| N38 | ALB-D-D12.7H0.79-N38 | D-D12.7H0.79-N38 Neodymium Magnets | 1.17 lbs (0.53kg) | Inquiry |
| N40 | ALB-D-D12.7H0.79-N40 | D-D12.7H0.79-N40 Neodymium Magnets | 1.27 lbs (0.58kg) | Inquiry |
| N42 | ALB-D-D12.7H0.79 | D-D12.7H0.79 Neodymium Magnets | 1.39 lbs (0.63kg) | Inquiry |
| N45 | ALB-D-D12.7H0.79-N45 | D-D12.7H0.79-N45 Neodymium Magnets | 1.48 lbs (0.67kg) | Inquiry |
| N48 | ALB-D-D12.7H0.79-N48 | D-D12.7H0.79-N48 Neodymium Magnets | 1.57 lbs (0.71kg) | Inquiry |
| N50 | ALB-D-D12.7H0.79-N50 | D-D12.7H0.79-N50 Neodymium Magnets | 1.61 lbs (0.73kg) | Inquiry |
| N52 | ALB-D-D12.7H0.79-N52 | D-D12.7H0.79-N52 Neodymium Magnets | 1.66 lbs (0.75kg) | Inquiry |
| N42SH | ALB-D-D12.7H0.79SH | D-D12.7H0.79SH Neodymium Magnets | 1.39 lbs (0.63kg) | Inquiry |
High Temperature D-D12.7H0.79 Neodymium Magnets (12.7mm dia. x 0.79mm thick) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
D-D12.7H0.79 Neodymium Magnets (12.7mm dia. x 0.79mm thick) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
Website: www.albmagnets.com
E-mail: sales@albmaterials.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.