- C-D5H10-N50 Neodymium Magnet, 5x10mm Cylinder Magnet
- BY062 Neodymium Magnets, 2 inch x 3/8 inch x 1/8 inch thick
- D62-N52 Neodymium Magnets, 3/8 inch dia. x 1/8 inch thick
- D5X8 Neodymium Magnets, 5/16 inch dia. x 1 1/2 inch thick
- D4x3.5mm Neodymium Magnet, 4 x 3.5mm Disc Magnet
- B50x10x1.5mm Neodymium Magnet, 50 x 10 x 1.5mm Block Magnet
- D84PC-WHT Plastic Coated Neodymium Magnets
- C-D3H5-N45 Neodymium Magnet, 3x5mm Cylinder Magnet
- C-D10H10-N50 Neodymium Magnet, 10x10mm Cylinder Magnet
- D19x2mm Neodymium Magnet, 19 x 2mm Disc Magnet
- Neodymium Ring & Tube Magnets Table
- 1/2 x 1/32 inch neodymium rare earth disc craft magnets n48 with 3m self-adhesive
- 125 Lb Pull Rare Earth Magnet
- Block Magnets
- 1/4 inch 6.35mm cube magnets
- 8mm Neodymium Magnet
- Ceramic Magnet Pull Force
- 25mm diameter magnet
- Use Of Neodymium Magnet
- 10 Examples Of Permanent Magnets
C-D5H8-N42UH Neodymium Magnet, 5x8mm Cylinder Magnet
| Item No.: | ALB-C-D5H8-N42UH |
|---|---|
| Material: | NdFeB, Grade N42UH |
| Shape: | Cylinder |
| Dimension: | 5mm dia. x 8mm thick |
| Tolerances: | ±0.1mm x ±0.1mm |
| Weight: | 1.178g |
| Grade: | N42UH |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 4.49 lbs (2.04kg) |
| Surface Field(Gauss): | 6300 Gauss |
| Magnetization direction: | Axial (Poles on Flat Ends) |
| Max Operating Temp: | 180ºC |
| Product Drawing: |  ·  |
Previous: C-D5H8-N35 Neodymium Magnet, 5x8mm Cylinder Magnet
Next: C-D5H8-N45 Neodymium Magnet, 5x8mm Cylinder Magnet
Related Magnets
C-D5H10-N35 Neodymium Magnet, 5x10mm Cylinder Magnet
C-D5H12-N45 Neodymium Magnet, 5x12mm Cylinder MagnetOther Grade C-D5H8 Neodymium Magnets (5mm dia. x 8mm thick):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-C-D5H8-N35 | C-D5H8-N35 Neodymium Magnets | 3.77 lbs (1.71kg) | Inquiry |
| N38 | ALB-C-D5H8-N38 | C-D5H8-N38 Neodymium Magnets | 3.77 lbs (1.71kg) | Inquiry |
| N40 | ALB-C-D5H8-N40 | C-D5H8-N40 Neodymium Magnets | 4.09 lbs (1.86kg) | Inquiry |
| N42 | ALB-C-D5H8 | C-D5H8 Neodymium Magnets | 4.49 lbs (2.04kg) | Inquiry |
| N45 | ALB-C-D5H8-N45 | C-D5H8-N45 Neodymium Magnets | 4.77 lbs (2.17kg) | Inquiry |
| N48 | ALB-C-D5H8-N48 | C-D5H8-N48 Neodymium Magnets | 5.05 lbs (2.30kg) | Inquiry |
| N50 | ALB-C-D5H8-N50 | C-D5H8-N50 Neodymium Magnets | 5.20 lbs (2.36kg) | Inquiry |
| N52 | ALB-C-D5H8-N52 | C-D5H8-N52 Neodymium Magnets | 5.34 lbs (2.43kg) | Inquiry |
| N42SH | ALB-C-D5H8SH | C-D5H8SH Neodymium Magnets | 4.49 lbs (2.04kg) | Inquiry |
High Temperature C-D5H8 Neodymium Magnets (5mm dia. x 8mm thick) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
C-D5H8 Neodymium Magnets (5mm dia. x 8mm thick) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
Website: www.albmagnets.com
E-mail: sales@albmaterials.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.