C-D12H12-N45 Neodymium Magnet, 12x12mm Cylinder Magnet

Item No.: ALB-C-D12H12-N45
Material: NdFeB, Grade N45
Shape: Cylinder
Dimension: 12mm dia. x 12mm thick
Tolerances: ±0.1mm x ±0.1mm
Weight: 10.179g
Grade: N45
Coating: Ni-Cu-Ni (Nickel)
Pull Force(lbs): 19.88 lbs (9.04kg)
Surface Field(Gauss): 6082 Gauss
Magnetization direction: Axial (Poles on Flat Ends)
Max Operating Temp: 80ºC
Product Drawing: PDF drawing of ALB-C-D12H12-N45 · JPEG drawing of ALB-C-D12H12-N45

Other Grade C-D12H12 Neodymium Magnets (12mm dia. x 12mm thick):

Grade Item No. Product Name Pull Force Inquiry
N35 ALB-C-D12H12-N35 C-D12H12-N35 Neodymium Magnets 15.74 lbs (7.15kg) Inquiry
N38 ALB-C-D12H12-N38 C-D12H12-N38 Neodymium Magnets 15.74 lbs (7.15kg) Inquiry
N40 ALB-C-D12H12-N40 C-D12H12-N40 Neodymium Magnets 17.06 lbs (7.76kg) Inquiry
N42 ALB-C-D12H12 C-D12H12 Neodymium Magnets 18.73 lbs (8.51kg) Inquiry
N45 ALB-C-D12H12-N45 C-D12H12-N45 Neodymium Magnets 19.88 lbs (9.04kg) Inquiry
N48 ALB-C-D12H12-N48 C-D12H12-N48 Neodymium Magnets 21.07 lbs (9.58kg) Inquiry
N50 ALB-C-D12H12-N50 C-D12H12-N50 Neodymium Magnets 21.67 lbs (9.85kg) Inquiry
N52 ALB-C-D12H12-N52 C-D12H12-N52 Neodymium Magnets 22.29 lbs (10.13kg) Inquiry
N42SH ALB-C-D12H12SH C-D12H12SH Neodymium Magnets 18.73 lbs (8.51kg) Inquiry

High Temperature C-D12H12 Neodymium Magnets (12mm dia. x 12mm thick) are also available:

Neodymium Material Type Maximum Operating Temp Curie Temp
N (N35-N52) 176°F (80°C) 590°F (310°C)
NM (N35M-N52M) 212°F (100°C) 644°F (340°C)
NH (N33H-N52H) 248°F (120°C) 644°F (340°C)
NSH (N30SH-N50SH) 302°F (150°C) 644°F (340°C)
NUH (N28UH-N48UH) 356°F (180°C) 662°F (350°C)
NEH (N28EH-N48EH) 392°F (200°C) 662°F (350°C)
NAH (N28AH-N35AH) 428°F (220°C) 662°F (350°C)

The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material.  Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.  

C-D12H12 Neodymium Magnets (12mm dia. x 12mm thick) with other Coating are also available:

Coating Type Overall Thickness Salt Spray Test Pressure Cooker Test
Ni-Cu-Ni (Nickel) 15-21 μm 24 hours 48 hours
NiCu + Black Nickel 15-21 μm 24 hours 48 hours
NiCuNi + Epoxy 20-28 μm 48 hours 72 hours
NiCuNi + Gold 16-23 μm 36 hours 72 hours
NiCuNi + Silver 16-23 μm 24 hours 48 hours
Zinc 7-15 μm 12 hours 24 hours

Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.

If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!

  • Not clear? Click to refresh.

How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.

Can't Find The Magnets You Need?