2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
United States
E-mail: sales@albmagnets.com
- B20x20x20mm Neodymium Magnet, 20 x 20 x 20mm Block Magnet
- D46 Neodymium Magnets, 1/4 inch dia. x 3/8 inch thick
- RX038DCB Neodymium Magnets, 1 inch od x 0.195 inch id x 0.375 inch id x 1/2 inch thick
- BCC8-N52 Neodymium Magnets, 3/4 inch x 3/4 inch x 1/2 inch thick
- R8201 Neodymium Magnets, 1/2 inch od x 1/8 inch id x 1/32 inch thick
- D55 Neodymium Magnets, 5/16 inch dia. x 5/16 inch thick
- DY05 Neodymium Magnets, 2 inch dia. x 5/16 inch thick
- RY04X0 Neodymium Magnets, 2 inch od x 1/4 inch id x 1 inch thick
- D9x1mm Neodymium Magnet, 9 x 1mm Disc Magnet
- D57 Neodymium Magnets, 5/16 inch dia. x 7/16 inch thick
- Where To Buy Rare Earth Neodymium Magnets?
- An Attractive Property Of The Magnet
- Best Cheap Fishing Magnet
- Neodymium Disc Magnets Table
- 1000Pcs 5mm Magnetic Balls
- Unique Motor Uses Only Permanent Magnets
- Brute Magnetics Double Sided
- Buy Magnets
- Education Science Experiment Tools Magnets
- Bar Magnets For School
B-W10H5L10-N45 Neodymium Magnet, 10x10x5mm Block Magnet
| Item No.: | ALB-B-W10H5L10-N45 |
|---|---|
| Material: | NdFeB, Grade N45 |
| Shape: | Block |
| Dimension: | 10x10x5mm |
| Tolerances: | ±0.1mm x ±0.1mm x ±0.1mm |
| Weight: | 3.750g |
| Grade: | N45 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 8.31 lbs (3.78kg) |
| Surface Field(Gauss): | 4532 Gauss |
| Magnetization direction: | Through Thickness |
| Max Operating Temp: | 80ºC |
| Product Drawing: |  ·  |
Previous: B-W10H3L20-N48 Neodymium Magnet, 20x10x3mm Block Magnet
Next: B-W10H5L14-N48M Neodymium Magnet, 14x10x5mm Block Magnet
Related Magnets
B-W10H5L30-N35 Neodymium Magnet, 30x10x5mm Block Magnet
B-W10H5L50-N45 Neodymium Magnet, 50x10x5mm Block Magnet
B-W10H8L55-N48BE Neodymium Magnet, 55x10x8mm Block Magnet
B-W11H5L35-N52 Neodymium Magnet, 35x11x5mm Block MagnetOther Grade B-W10H10L5 Neodymium Magnets (10x10x5mm):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-B-W10H10L5-N35 | B-W10H10L5-N35 Neodymium Magnets | 6.58 lbs (2.99kg) | Inquiry |
| N38 | ALB-B-W10H10L5-N38 | B-W10H10L5-N38 Neodymium Magnets | 6.58 lbs (2.99kg) | Inquiry |
| N40 | ALB-B-W10H10L5-N40 | B-W10H10L5-N40 Neodymium Magnets | 7.14 lbs (3.24kg) | Inquiry |
| N42 | ALB-B-W10H10L5 | B-W10H10L5 Neodymium Magnets | 7.83 lbs (3.56kg) | Inquiry |
| N45 | ALB-B-W10H10L5-N45 | B-W10H10L5-N45 Neodymium Magnets | 8.31 lbs (3.78kg) | Inquiry |
| N48 | ALB-B-W10H10L5-N48 | B-W10H10L5-N48 Neodymium Magnets | 8.81 lbs (4.00kg) | Inquiry |
| N50 | ALB-B-W10H10L5-N50 | B-W10H10L5-N50 Neodymium Magnets | 9.06 lbs (4.12kg) | Inquiry |
| N52 | ALB-B-W10H10L5-N52 | B-W10H10L5-N52 Neodymium Magnets | 9.32 lbs (4.24kg) | Inquiry |
| N42SH | ALB-B-W10H10L5SH | B-W10H10L5SH Neodymium Magnets | 7.83 lbs (3.56kg) | Inquiry |
High Temperature B-W10H10L5 Neodymium Magnets (10x10x5mm) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
B-W10H10L5 Neodymium Magnets (10x10x5mm) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
Website: www.albmagnets.com
E-mail: sales@albmagnets.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.