B55x10x8mm Neodymium Magnet, 55 x 10 x 8mm Block Magnet

Item No.: ALB-B55x10x8mm
Material: NdFeB, Grade N42
Shape: Block
Dimension: 55x10x8mm
Tolerances: ±0.1mm x ±0.1mm x ±0.1mm
Weight: 33.000g
Grade: N42
Coating: Ni-Cu-Ni (Nickel)
Pull Force(lbs): 29.39 lbs (13.36kg)
Surface Field(Gauss): 4356
Magnetization direction: Through Thickness
Max Operating Temp: 80°C
Product Drawing: PDF drawing of ALB-B55x10x8mm · JPEG drawing of ALB-B55x10x8mm

Other Grade B55x10x8mm Neodymium Magnets (55x10x8mm):

Grade Item No. Product Name Pull Force Inquiry
N35 ALB-B55x10x8mm-N35 B55x10x8mm-N35 Neodymium Magnets 24.69 lbs (11.22kg) Inquiry
N38 ALB-B55x10x8mm-N38 B55x10x8mm-N38 Neodymium Magnets 24.69 lbs (11.22kg) Inquiry
N40 ALB-B55x10x8mm-N40 B55x10x8mm-N40 Neodymium Magnets 26.78 lbs (12.17kg) Inquiry
N42 ALB-B55x10x8mm B55x10x8mm Neodymium Magnets 29.39 lbs (13.36kg) Inquiry
N45 ALB-B55x10x8mm-N45 B55x10x8mm-N45 Neodymium Magnets 31.20 lbs (14.18kg) Inquiry
N48 ALB-B55x10x8mm-N48 B55x10x8mm-N48 Neodymium Magnets 33.06 lbs (15.03kg) Inquiry
N50 ALB-B55x10x8mm-N50 B55x10x8mm-N50 Neodymium Magnets 34.01 lbs (15.46kg) Inquiry
N52 ALB-B55x10x8mm-N52 B55x10x8mm-N52 Neodymium Magnets 34.97 lbs (15.90kg) Inquiry
N42SH ALB-B55x10x8mmSH B55x10x8mmSH Neodymium Magnets 29.39 lbs (13.36kg) Inquiry

High Temperature B55x10x8mm Neodymium Magnets (55x10x8mm) are also available:

Neodymium Material Type Maximum Operating Temp Curie Temp
N (N35-N52) 176°F (80°C) 590°F (310°C)
NM (N35M-N52M) 212°F (100°C) 644°F (340°C)
NH (N33H-N52H) 248°F (120°C) 644°F (340°C)
NSH (N30SH-N50SH) 302°F (150°C) 644°F (340°C)
NUH (N28UH-N48UH) 356°F (180°C) 662°F (350°C)
NEH (N28EH-N48EH) 392°F (200°C) 662°F (350°C)
NAH (N28AH-N35AH) 428°F (220°C) 662°F (350°C)

The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material.  Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.  

B55x10x8mm Neodymium Magnets (55x10x8mm) with other Coating are also available:

Coating Type Overall Thickness Salt Spray Test Pressure Cooker Test
Ni-Cu-Ni (Nickel) 15-21 μm 24 hours 48 hours
NiCu + Black Nickel 15-21 μm 24 hours 48 hours
NiCuNi + Epoxy 20-28 μm 48 hours 72 hours
NiCuNi + Gold 16-23 μm 36 hours 72 hours
NiCuNi + Silver 16-23 μm 24 hours 48 hours
Zinc 7-15 μm 12 hours 24 hours

Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.

If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!

  • Not clear? Click to refresh.

How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.

Can't Find The Magnets You Need?