2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
United States
E-mail: sales@albmagnets.com
- D8x1mm Neodymium Magnet, 8 x 1mm Disc Magnet
- D24x4mm Neodymium Magnet, 24 x 4mm Disc Magnet
- RY04Y0 Neodymium Magnets, 2 inch od x 1/4 inch id x 2 inch thick
- DX4Y8 Neodymium Magnets, 1 1/4 inch dia. x 2 1/2 inch thick
- D8X2 Neodymium Magnets, 1/2 inch dia. x 1 1/8 inch thick
- SB483-IN Neodymium Magnets, 1/4 inch length x 1/2 inch width x 3/16 inch thick, with step IN
- B775 Neodymium Magnets, 7/16 inch x 7/16 inch x 5/16 inch thick
- B8801 Neodymium Magnets, 1/2 inch x 1/2 inch x 1/32 inch thick
- DX28 Neodymium Magnets, 1 1/8 inch dia. x 1/2 inch thick
- DZ0X0 Neodymium Magnets, 3 inch dia. x 1 inch thick
- 10 Weird And Wonderful Uses For Magnets
- Ring Magnets For Sale
- 1000 Lb Fishing Magnet
- Why Don't We Create A Permanent Magnet Of 1000 Tesla
- What are Rare Earth Magnets?
- Neodymium Sphere & Ball Magnets Table
- Ceramic Bar And Block Magnets
- 4 Differences Between Neodymium Magnets And Samarium Cobalt Magnets
- 5mm Magnetic Balls
- 2800 Tesla Magnetic Field
B4x2x1.34mm Neodymium Magnet, 4 x 2 x 1.34mm Block Magnet
| Item No.: | B4x2x1.34mm |
|---|---|
| Material: | NdFeB, Grade N42 |
| Shape: | Block |
| Dimension: | 4x2x1.34mm |
| Tolerances: | ±0.1mm x ±0.1mm x ±0.1mm |
| Weight: | 0.011g |
| Grade: | N42 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 0.59 lbs (0.27kg) |
| Surface Field(Gauss): | 4414 |
| Magnetization direction: | Through Thickness |
| Max Operating Temp: | 80°C |
| Product Drawing: |  ·  |
Previous: B3x3x3mm Neodymium Magnet, 3 x 3 x 3mm Block Magnet
Next: B4x3x1.8mm Neodymium Magnet, 4 x 3 x 1.8mm Block Magnet
Related Magnets
B4x4x1mm Neodymium Magnet, 4 x 4 x 1mm Block Magnet
B5x3x1mm Neodymium Magnet, 5 x 3 x 1mm Block Magnet
B5x3x1.7mm Neodymium Magnet, 5 x 3 x 1.7mm Block Magnet
B5x3x2mm Neodymium Magnet, 5 x 3 x 2mm Block MagnetOther Grade B4x2x1.34mm Neodymium Magnets (4x2x1.34mm):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-B4x2x1.34mm-N35 | B4x2x1.34mm-N35 Neodymium Magnets | 0.50 lbs (0.23kg) | Inquiry |
| N38 | ALB-B4x2x1.34mm-N38 | B4x2x1.34mm-N38 Neodymium Magnets | 0.50 lbs (0.23kg) | Inquiry |
| N40 | ALB-B4x2x1.34mm-N40 | B4x2x1.34mm-N40 Neodymium Magnets | 0.54 lbs (0.25kg) | Inquiry |
| N42 | ALB-B4x2x1.34mm | B4x2x1.34mm Neodymium Magnets | 0.59 lbs (0.27kg) | Inquiry |
| N45 | ALB-B4x2x1.34mm-N45 | B4x2x1.34mm-N45 Neodymium Magnets | 0.63 lbs (0.29kg) | Inquiry |
| N48 | ALB-B4x2x1.34mm-N48 | B4x2x1.34mm-N48 Neodymium Magnets | 0.67 lbs (0.30kg) | Inquiry |
| N50 | ALB-B4x2x1.34mm-N50 | B4x2x1.34mm-N50 Neodymium Magnets | 0.69 lbs (0.31kg) | Inquiry |
| N52 | ALB-B4x2x1.34mm-N52 | B4x2x1.34mm-N52 Neodymium Magnets | 0.71 lbs (0.32kg) | Inquiry |
| N42SH | ALB-B4x2x1.34mmSH | B4x2x1.34mmSH Neodymium Magnets | 0.59 lbs (0.27kg) | Inquiry |
High Temperature B4x2x1.34mm Neodymium Magnets (4x2x1.34mm) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
B4x2x1.34mm Neodymium Magnets (4x2x1.34mm) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
Website: www.albmagnets.com
E-mail: sales@albmagnets.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.