2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
United States
E-mail: sales@albmagnets.com
- BX021 Neodymium Magnets, 1 inch x 1/8 inch x 1/16 inch thick
- BZ0X02 Neodymium Magnets, 3 inch x 1 inch x 1/8 inch thick
- D15x1.5mm Neodymium Magnet, 15 x 1.5mm Disc Magnet
- DZ06 Neodymium Magnets, 3 inch dia. x 3/8 inch thick
- D3x1.5mm-N35 Neodymium Magnets
- DX04 Neodymium Magnets, 1 inch dia. x 1/4 inch thick
- B-W4.8H2.6L7.5-N50 Neodymium Magnet, 7.5x4.8x2.6mm Block Magnet
- D-D23.6H20-N42H Neodymium Magnet, 23.6x20mm Disc Magnet
- SDX06-IN Neodymium Magnets, 1 inch dia. x 3/8 inch thick with step IN
- S6B Neodymium Magnets, 3/8 inch diameter
- What are Rare Earth Magnets?
- Refrigerator Magnets For Sale
- 125 Lb Pull N52 Neodymium Magnets
- Neodymium Magnet Price
- 125 Lb Pull Rare Earth Magnet
- 5mm Magnetic Balls
- Permanent Magnets For Sale
- Education Science Experiment Tools Magnets
- 4 Differences Between Neodymium Magnets And Samarium Cobalt Magnets
- Magnetization Direction For Neodymium Magnets
B35x15x3mm Neodymium Magnet, 35 x 15 x 3mm Block Magnet
| Item No.: | ALB-B35x15x3mm |
|---|---|
| Material: | NdFeB, Grade N42 |
| Shape: | Block |
| Dimension: | 35x15x3mm |
| Tolerances: | ±0.1mm x ±0.1mm x ±0.1mm |
| Weight: | 11.813g |
| Grade: | N42 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 10.77 lbs (4.89kg) |
| Surface Field(Gauss): | 1741 |
| Magnetization direction: | Through Thickness |
| Max Operating Temp: | 80°C |
| Product Drawing: |  ·  |
Previous: B35x11x5mm Neodymium Magnet, 35 x 11 x 5mm Block Magnet
Next: B35x30x15mm Neodymium Magnet, 35 x 30 x 15mm Block Magnet
Related Magnets
B36x3.4x2.6mm Neodymium Magnet, 36 x 3.4 x 2.6mm Block Magnet
B39x9x5.5mm Neodymium Magnet, 39 x 9 x 5.5mm Block Magnet
B40x6x4mm Neodymium Magnet, 40 x 6 x 4mm Block Magnet
B40x10x1mm Neodymium Magnet, 40 x 10 x 1mm Block MagnetOther Grade B35x15x3mm Neodymium Magnets (35x15x3mm):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-B35x15x3mm-N35 | B35x15x3mm-N35 Neodymium Magnets | 9.05 lbs (4.11kg) | Inquiry |
| N38 | ALB-B35x15x3mm-N38 | B35x15x3mm-N38 Neodymium Magnets | 9.05 lbs (4.11kg) | Inquiry |
| N40 | ALB-B35x15x3mm-N40 | B35x15x3mm-N40 Neodymium Magnets | 9.81 lbs (4.46kg) | Inquiry |
| N42 | ALB-B35x15x3mm | B35x15x3mm Neodymium Magnets | 10.77 lbs (4.89kg) | Inquiry |
| N45 | ALB-B35x15x3mm-N45 | B35x15x3mm-N45 Neodymium Magnets | 11.43 lbs (5.20kg) | Inquiry |
| N48 | ALB-B35x15x3mm-N48 | B35x15x3mm-N48 Neodymium Magnets | 12.11 lbs (5.51kg) | Inquiry |
| N50 | ALB-B35x15x3mm-N50 | B35x15x3mm-N50 Neodymium Magnets | 12.46 lbs (5.66kg) | Inquiry |
| N52 | ALB-B35x15x3mm-N52 | B35x15x3mm-N52 Neodymium Magnets | 12.81 lbs (5.82kg) | Inquiry |
| N42SH | ALB-B35x15x3mmSH | B35x15x3mmSH Neodymium Magnets | 10.77 lbs (4.89kg) | Inquiry |
High Temperature B35x15x3mm Neodymium Magnets (35x15x3mm) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
B35x15x3mm Neodymium Magnets (35x15x3mm) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
Website: www.albmagnets.com
E-mail: sales@albmagnets.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.