2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
United States
E-mail: sales@albmagnets.com
- DZ0Y8 Neodymium Magnets, 3 inch dia. x 2 1/2 inch thick
- D96 Neodymium Magnets, 9/16 inch dia. x 3/8 inch thick
- B844 Neodymium Magnets, 1/2 inch x 1/4 inch x 1/4 inch thick
- B888PC-GRN Plastic Coated Neodymium Magnets
- D43-N52 Neodymium Magnets, 1/4 inch dia. x 3/16 inch thick
- DX2A Neodymium Magnets, 1 1/8 inch dia. x 5/8 inch thick
- D-D12H5-N42 Neodymium Magnet, 12x5mm Disc Magnet
- S5 Neodymium Magnets, 5/16 inch diameter
- D8x20mm Neodymium Magnet, 8 x 20mm Cylinder Magnet
- D8x1.5mm Neodymium Magnet, 8 x 1.5mm Disc Magnet
- Permanent Magnet And Electromagnets
- Neodymium Block & Bar Magnets Table
- Block Magnets
- 4 Differences Between Neodymium Magnets And Samarium Cobalt Magnets
- Glossary of Magnet Terminology
- 2800 Tesla Magnetic Field
- Custom Alnico Magnets
- Neodymium Cube Magnets Table
- Neodymium Magnets Applications
- Bar Magnet Uses
D22x6mm Neodymium Magnet, 22 x 6mm Disc Magnet
| Item No.: | ALB-D22x6mm |
|---|---|
| Material: | NdFeB, Grade N42 |
| Shape: | Disc |
| Dimension: | 22mm dia. x 6mm thick |
| Tolerances: | ±0.1mm x ±0.1mm |
| Weight: | 17.106g |
| Grade: | N42 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 18.32 lbs (8.33kg) |
| Surface Field(Gauss): | 3160 Gauss |
| Magnetization direction: | Axial (Poles on Flat Ends) |
| Max Operating Temp: | 80°C |
| Product Drawing: |  ·  |
Previous: D22x2mm Neodymium Magnet, 22 x 2mm Disc Magnet
Next: D22x20mm Neodymium Magnet, 22 x 20mm Disc Magnet
Related Magnets
D23x20mm Neodymium Magnet, 23 x 20mm Disc Magnet
D24x4mm Neodymium Magnet, 24 x 4mm Disc Magnet
D24x5mm Neodymium Magnet, 24 x 5mm Disc Magnet
D24x16mm Neodymium Magnet, 24 x 16mm Disc MagnetOther Grade D22x6mm Neodymium Magnets (22mm dia. x 6mm thick):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-D22x6mm-N35 | D22x6mm-N35 Neodymium Magnets | 15.39 lbs (7.00kg) | Inquiry |
| N38 | ALB-D22x6mm-N38 | D22x6mm-N38 Neodymium Magnets | 15.39 lbs (7.00kg) | Inquiry |
| N40 | ALB-D22x6mm-N40 | D22x6mm-N40 Neodymium Magnets | 16.69 lbs (7.59kg) | Inquiry |
| N42 | ALB-D22x6mm | D22x6mm Neodymium Magnets | 18.32 lbs (8.33kg) | Inquiry |
| N45 | ALB-D22x6mm-N45 | D22x6mm-N45 Neodymium Magnets | 19.45 lbs (8.84kg) | Inquiry |
| N48 | ALB-D22x6mm-N48 | D22x6mm-N48 Neodymium Magnets | 20.61 lbs (9.37kg) | Inquiry |
| N50 | ALB-D22x6mm-N50 | D22x6mm-N50 Neodymium Magnets | 21.20 lbs (9.64kg) | Inquiry |
| N52 | ALB-D22x6mm-N52 | D22x6mm-N52 Neodymium Magnets | 21.80 lbs (9.91kg) | Inquiry |
| N42SH | ALB-D22x6mmSH | D22x6mmSH Neodymium Magnets | 18.32 lbs (8.33kg) | Inquiry |
High Temperature D22x6mm Neodymium Magnets (22mm dia. x 6mm thick) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
D22x6mm Neodymium Magnets (22mm dia. x 6mm thick) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
Website: www.albmagnets.com
E-mail: sales@albmagnets.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.