Magnets Home > Products > Neodymium Magnets > Cylinder > D15x25mm Neodymium Magnet, 15 x 25mm Cylinder Magnet

D15x25mm Neodymium Magnet, 15 x 25mm Cylinder Magnet

Inquiry

Item No.:	D15x25mm
Material:	NdFeB, Grade N42
Shape:	Cylinder
Dimension:	15mm dia. x 25mm thick
Tolerances:	±0.1mm x ±0.1mm
Weight:	33.134g
Grade:	N42
Coating:	Ni-Cu-Ni (Nickel)
Pull Force(lbs):	36.95 lbs (16.79kg)
Surface Field(Gauss):	6322 Gauss
Magnetization direction:	Axial (Poles on Flat Ends)
Max Operating Temp:	80°C
Product Drawing:	·

Previous: D15x15mm Neodymium Magnet, 15 x 15mm Cylinder Magnet

Next: D15x30mm Neodymium Magnet, 15 x 30mm Cylinder Magnet

Related Magnets

Other Grade D15x25mm Neodymium Magnets (15mm dia. x 25mm thick):

Grade	Item No.	Product Name	Pull Force	Inquiry
N35	ALB-D15x25mm-N35	D15x25mm-N35 Neodymium Magnets	31.04 lbs (14.11kg)	Inquiry
N38	ALB-D15x25mm-N38	D15x25mm-N38 Neodymium Magnets	31.04 lbs (14.11kg)	Inquiry
N40	ALB-D15x25mm-N40	D15x25mm-N40 Neodymium Magnets	33.66 lbs (15.30kg)	Inquiry
N42	ALB-D15x25mm	D15x25mm Neodymium Magnets	36.95 lbs (16.79kg)	Inquiry
N45	ALB-D15x25mm-N45	D15x25mm-N45 Neodymium Magnets	39.22 lbs (17.83kg)	Inquiry
N48	ALB-D15x25mm-N48	D15x25mm-N48 Neodymium Magnets	41.56 lbs (18.89kg)	Inquiry
N50	ALB-D15x25mm-N50	D15x25mm-N50 Neodymium Magnets	42.76 lbs (19.43kg)	Inquiry
N52	ALB-D15x25mm-N52	D15x25mm-N52 Neodymium Magnets	43.97 lbs (19.99kg)	Inquiry
N42SH	ALB-D15x25mmSH	D15x25mmSH Neodymium Magnets	36.95 lbs (16.79kg)	Inquiry

High Temperature D15x25mm Neodymium Magnets (15mm dia. x 25mm thick) are also available:

Neodymium Material Type	Maximum Operating Temp	Curie Temp
N (N35-N52)	176°F (80°C)	590°F (310°C)
NM (N35M-N52M)	212°F (100°C)	644°F (340°C)
NH (N33H-N52H)	248°F (120°C)	644°F (340°C)
NSH (N30SH-N50SH)	302°F (150°C)	644°F (340°C)
NUH (N28UH-N48UH)	356°F (180°C)	662°F (350°C)
NEH (N28EH-N48EH)	392°F (200°C)	662°F (350°C)
NAH (N28AH-N35AH)	428°F (220°C)	662°F (350°C)

The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.

D15x25mm Neodymium Magnets (15mm dia. x 25mm thick) with other Coating are also available:

Coating Type	Overall Thickness	Salt Spray Test	Pressure Cooker Test
Ni-Cu-Ni (Nickel)	15-21 μm	24 hours	48 hours
NiCu + Black Nickel	15-21 μm	24 hours	48 hours
NiCuNi + Epoxy	20-28 μm	48 hours	72 hours
NiCuNi + Gold	16-23 μm	36 hours	72 hours
NiCuNi + Silver	16-23 μm	24 hours	48 hours
Zinc	7-15 μm	12 hours	24 hours

Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.

If you can't find what you want, just send us an inquiry and we will be happy to make it for you!