B12x6x4mm Neodymium Magnet, 12 x 6 x 4mm Block Magnet

Item No.: B12x6x4mm
Material: NdFeB, Grade N42
Shape: Block
Dimension: 12x6x4mm
Tolerances: ±0.1mm x ±0.1mm x ±0.1mm
Weight: 0.288g
Grade: N42
Coating: Ni-Cu-Ni (Nickel)
Pull Force(lbs): 5.32 lbs (2.42kg)
Surface Field(Gauss): 4403
Magnetization direction: Through Thickness
Max Operating Temp: 80°C
Product Drawing: PDF drawing of B12x6x4mm · JPEG drawing of B12x6x4mm

Other Grade B12x6x4mm Neodymium Magnets (12x6x4mm):

Grade Item No. Product Name Pull Force Inquiry
N35 ALB-B12x6x4mm-N35 B12x6x4mm-N35 Neodymium Magnets 4.47 lbs (2.03kg) Inquiry
N38 ALB-B12x6x4mm-N38 B12x6x4mm-N38 Neodymium Magnets 4.47 lbs (2.03kg) Inquiry
N40 ALB-B12x6x4mm-N40 B12x6x4mm-N40 Neodymium Magnets 4.84 lbs (2.20kg) Inquiry
N42 ALB-B12x6x4mm B12x6x4mm Neodymium Magnets 5.32 lbs (2.42kg) Inquiry
N45 ALB-B12x6x4mm-N45 B12x6x4mm-N45 Neodymium Magnets 5.64 lbs (2.57kg) Inquiry
N48 ALB-B12x6x4mm-N48 B12x6x4mm-N48 Neodymium Magnets 5.98 lbs (2.72kg) Inquiry
N50 ALB-B12x6x4mm-N50 B12x6x4mm-N50 Neodymium Magnets 6.15 lbs (2.80kg) Inquiry
N52 ALB-B12x6x4mm-N52 B12x6x4mm-N52 Neodymium Magnets 6.33 lbs (2.88kg) Inquiry
N42SH ALB-B12x6x4mmSH B12x6x4mmSH Neodymium Magnets 5.32 lbs (2.42kg) Inquiry

High Temperature B12x6x4mm Neodymium Magnets (12x6x4mm) are also available:

Neodymium Material Type Maximum Operating Temp Curie Temp
N (N35-N52) 176°F (80°C) 590°F (310°C)
NM (N35M-N52M) 212°F (100°C) 644°F (340°C)
NH (N33H-N52H) 248°F (120°C) 644°F (340°C)
NSH (N30SH-N50SH) 302°F (150°C) 644°F (340°C)
NUH (N28UH-N48UH) 356°F (180°C) 662°F (350°C)
NEH (N28EH-N48EH) 392°F (200°C) 662°F (350°C)
NAH (N28AH-N35AH) 428°F (220°C) 662°F (350°C)

The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material.  Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.  

B12x6x4mm Neodymium Magnets (12x6x4mm) with other Coating are also available:

Coating Type Overall Thickness Salt Spray Test Pressure Cooker Test
Ni-Cu-Ni (Nickel) 15-21 μm 24 hours 48 hours
NiCu + Black Nickel 15-21 μm 24 hours 48 hours
NiCuNi + Epoxy 20-28 μm 48 hours 72 hours
NiCuNi + Gold 16-23 μm 36 hours 72 hours
NiCuNi + Silver 16-23 μm 24 hours 48 hours
Zinc 7-15 μm 12 hours 24 hours

Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.

If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!

  • Not clear? Click to refresh.

How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.

Can't Find The Magnets You Need?