2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
United States
E-mail: sales@albmagnets.com
- S5 Neodymium Magnets, 5/16 inch diameter
- DEH1 Neodymium Magnets, 7/8 inch dia. x 1/10 inch thick
- STIR25 Neodymium Stir Bar, 0.315 inch dia. x 0.984 inch long (8mm dia. x 25mm long)
- RX04X0 Neodymium Magnets, 1 inch od x 1/4 inch id x 1 inch thick
- BX8C4-N52 Neodymium Magnets, 1 1/2 inch x 3/4 inch x 1/4 inch thick
- DH24 Neodymium Magnets, 2/10 inch dia. x 1/4 inch thick
- B30x20x2mm Neodymium Magnet, 30 x 20 x 2mm Block Magnet
- B25x10x5mm Neodymium Magnet, 25 x 10 x 5mm Block Magnet
- SB443-IN Neodymium Magnets, 1/4 inch length x 1/4 inch width x 3/16 inch thick, with step IN
- DY8Y0 Neodymium Magnets, 2 1/2 inch dia. x 2 inch thick
- Education Science Experiment Tools Magnets
- A Magnet Attracts A Piece Of Iron
- 125 Lb Pull N52 Neodymium Magnets
- Neodymium Magnet Price
- Characteristics Of Magnets Worksheet Answers
- Permanent Magnets For Sale
- Ceramic Magnet Pull Force
- Application Of Magnet
- 1000Pcs 5mm Magnetic Balls
- Bar Magnets For Sale
B10x2.8x1.9mm Neodymium Magnet, 10 x 2.8 x 1.9mm Block Magnet
| Item No.: | B10x2.8x1.9mm |
|---|---|
| Material: | NdFeB, Grade N42 |
| Shape: | Block |
| Dimension: | 10x2.8x1.9mm |
| Tolerances: | ±0.1mm x ±0.1mm x ±0.1mm |
| Weight: | 0.053g |
| Grade: | N42 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 1.57 lbs (0.72kg) |
| Surface Field(Gauss): | 4129 |
| Magnetization direction: | Through Thickness |
| Max Operating Temp: | 80°C |
| Product Drawing: |  ·  |
Previous: B10x1.6x0.7mm Neodymium Magnet, 10 x 1.6 x 0.7mm Block Magnet
Next: B10x2.8x2.5mm Neodymium Magnet, 10 x 2.8 x 2.5mm Block Magnet
Related Magnets
B10x3x1mm Neodymium Magnet, 10 x 3 x 1mm Block Magnet
B10x3x2mm Neodymium Magnet, 10 x 3 x 2mm Block Magnet
B10x3.3x2.3mm Neodymium Magnet, 10 x 3.3 x 2.3mm Block Magnet
B10x5x1mm Neodymium Magnet, 10 x 5 x 1mm Block MagnetOther Grade B10x2.8x1.9mm Neodymium Magnets (10x2.8x1.9mm):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-B10x2.8x1.9mm-N35 | B10x2.8x1.9mm-N35 Neodymium Magnets | 1.32 lbs (0.60kg) | Inquiry |
| N38 | ALB-B10x2.8x1.9mm-N38 | B10x2.8x1.9mm-N38 Neodymium Magnets | 1.32 lbs (0.60kg) | Inquiry |
| N40 | ALB-B10x2.8x1.9mm-N40 | B10x2.8x1.9mm-N40 Neodymium Magnets | 1.43 lbs (0.65kg) | Inquiry |
| N42 | ALB-B10x2.8x1.9mm | B10x2.8x1.9mm Neodymium Magnets | 1.57 lbs (0.72kg) | Inquiry |
| N45 | ALB-B10x2.8x1.9mm-N45 | B10x2.8x1.9mm-N45 Neodymium Magnets | 1.67 lbs (0.76kg) | Inquiry |
| N48 | ALB-B10x2.8x1.9mm-N48 | B10x2.8x1.9mm-N48 Neodymium Magnets | 1.77 lbs (0.81kg) | Inquiry |
| N50 | ALB-B10x2.8x1.9mm-N50 | B10x2.8x1.9mm-N50 Neodymium Magnets | 1.82 lbs (0.83kg) | Inquiry |
| N52 | ALB-B10x2.8x1.9mm-N52 | B10x2.8x1.9mm-N52 Neodymium Magnets | 1.87 lbs (0.85kg) | Inquiry |
| N42SH | ALB-B10x2.8x1.9mmSH | B10x2.8x1.9mmSH Neodymium Magnets | 1.57 lbs (0.72kg) | Inquiry |
High Temperature B10x2.8x1.9mm Neodymium Magnets (10x2.8x1.9mm) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
B10x2.8x1.9mm Neodymium Magnets (10x2.8x1.9mm) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
If you can't find what you want, just send us an inquiry and we will be happy to make it for you!
Send us an inquiry now to find out more information and the latest prices, thanks!
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
Website: www.albmagnets.com
E-mail: sales@albmagnets.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.