2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
United States
E-mail: sales@albmagnets.com
- B888-2PA-N52 Neodymium Magnets, 1/2" x 1/2"x 1/2" (- 0.127" hole) Hole parallel to magnetization direction
- DA4-N52 Neodymium Magnets, 5/8" dia. x 1/4" thick
- DY04 Neodymium Magnets, 2" dia. x 1/4" thick
- MM-B-25 Metric Mounting Magnets
- DX4A Neodymium Magnets, 1 1/4" dia. x 5/8" thick
- R414CLB Neodymium Magnets, 1/4"od x (1/10" x 1/21")x 1/4"
- B663 Neodymium Block Magnets
- DX8X4 Neodymium Magnets, 1 1/2" dia. x 1 1/4" thick
- D42E Neodymium Magnets, 1/4" dia. x 1/8" thick
- RX054TP-N52 Plastic Coated Neodymium Magnets
- What Are The Magnets
- Neodymium Magnets Production
- What are Rare Earth Magnets?
- 81mm Round Magnet
- 4 Differences Between Neodymium Magnets And Samarium Cobalt Magnets
- 5x1 N48 Magnets
- Neodymium Cylinder Magnets Table
- Scientists Create Ultra-Powerful Magnetic Field
- 2 Neodymium Magnets
- What are neodymium magnets?
BCC2-N52 Neodymium Magnets, 3/4" x 3/4" x 1/8" thick
| Item No.: | ALB-BCC2-N52 |
|---|---|
| Material: | NdFeB, Grade N52 |
| Shape: | Block |
| Dimension: | 3/4" x 3/4" x 1/8" thick |
| Tolerances: | ±0.004" x ±0.004" x ±0.004" |
| Weight: | 8.64 g |
| Grade: | N52 |
| Coating: | Ni-Cu-Ni (Nickel) |
| Pull Force(lbs): | 13.53 lbs |
| Surface Field(Gauss): | 2125 Gauss |
| Magnetization direction: | Through Thickness |
| Max Operating Temp: | 80°C |
Previous: BCC2 Neodymium Magnets, 3/4" x 3/4" x 1/8" thick
Next: BCC3 Neodymium Magnets, 3/4" x 3/4" x 3/16" thick
Related Magnets
BX8X84 Neodymium Magnets, 1 1/2" x 1 1/2" x 1/4" thick
B84H1 Neodymium Magnets, 1/2" x 1/4" x 1/10" thick
BCCA Neodymium Magnets, 3/4" x 3/4" x 5/8" thick
B665 Neodymium Magnets, 3/8" x 3/8" x 5/16" thickOther Grade BCC2 Neodymium Magnets (3/4" x 3/4" x 1/8" thick):
| Grade | Item No. | Product Name | Pull Force | Inquiry |
|---|---|---|---|---|
| N35 | ALB-BCC2-N35 | BCC2-N35 Neodymium Magnets | 7.96 lbs | Inquiry |
| N38 | ALB-BCC2-N38 | BCC2-N38 Neodymium Magnets | 7.96 lbs | Inquiry |
| N40 | ALB-BCC2-N40 | BCC2-N40 Neodymium Magnets | 8.63 lbs | Inquiry |
| N42 | ALB-BCC2 | BCC2 Neodymium Magnets | 9.47 lbs | Inquiry |
| N45 | ALB-BCC2-N45 | BCC2-N45 Neodymium Magnets | 10.21 lbs | Inquiry |
| N48 | ALB-BCC2-N48 | BCC2-N48 Neodymium Magnets | 10.96 lbs | Inquiry |
| N50 | ALB-BCC2-N50 | BCC2-N50 Neodymium Magnets | 11.43 lbs | Inquiry |
| N52 | ALB-BCC2-N52 | BCC2-N52 Neodymium Magnets | 11.91 lbs | Inquiry |
| N42SH | ALB-BCC2SH | BCC2SH Neodymium Magnets | 9.47 lbs | Inquiry |
High Temperature BCC2 Neodymium Magnets (3/4" x 3/4" x 1/8" thick) are also available:
| Neodymium Material Type | Maximum Operating Temp | Curie Temp |
|---|---|---|
| N (N35-N52) | 176°F (80°C) | 590°F (310°C) |
| NM (N35M-N52M) | 212°F (100°C) | 644°F (340°C) |
| NH (N33H-N52H) | 248°F (120°C) | 644°F (340°C) |
| NSH (N30SH-N50SH) | 302°F (150°C) | 644°F (340°C) |
| NUH (N28UH-N48UH) | 356°F (180°C) | 662°F (350°C) |
| NEH (N28EH-N48EH) | 392°F (200°C) | 662°F (350°C) |
| NAH (N28AH-N35AH) | 428°F (220°C) | 662°F (350°C) |
The Thermal Characteristics listed above are values commonly associated with each magnet's grade or material. Actual performance in your application may vary with other factors, including the shape of the magnet, the Permeance Coefficient or load line, and how it is used in a circuit.
BCC2 Neodymium Magnets (3/4" x 3/4" x 1/8" thick) with other Coating are also available:
| Coating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
|---|---|---|---|
| Ni-Cu-Ni (Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver Coating layers are 1-2 μm thick. Test results shown to allow comparison between Coating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
Company
About Us
Privacy Policy
Terms & Conditions
XML Sitemap
HTML SitemapCustomer Support
Inquiry
FAQ
How To Order
Shipment TrackingFeatured Magnets
Neodymium Magnets
Micro Magnets
Custom MagnetsPopular Magnets
Grade N42 Magnets
Grade N52 Magnets
Magnets Pull Force Calculator
Contact Us
ALB Materials Inc
2360 Corporate Circle. Suite 400
Henderson, NV 89074-7739
Website: www.albmagnets.com
E-mail: sales@albmagnets.com
How to choose and buy a strong neodymium magnet? ALBMagnets is a professional company for strong magnet design and manufacturing,
providing you with reliable N35, N38, N42, N52, N42SH and other grade super neodymium magnets and SmCo rare earth magnets.